Special Price for Graphite Electrode Plant - HP 350mm Graphite Electrode – Hexi
Special Price for Graphite Electrode Plant - HP 350mm Graphite Electrode – Hexi Detail:
HP graphite electrode is mainly made of petroleum coke and needle coke, It is capable of carrying the current density 18-25A/cm2. Generally it is designed for high power electric arc furnace steel-making.
| Comparison Technical Specification for HP Graphite Electrode 14″ | ||
| Electrode | ||
| Item | Unit | Supplier Spec |
| Typical Characteristics of Pole | ||
| Nominal Diameter | mm | 350 |
| Max Diameter | mm | 358 |
| Min Diameter | mm | 352 |
| Nominal Length | mm | 1600/1800 |
| Max Length | mm | 1700/1900 |
| Min Length | mm | 1500/1700 |
| Bulk Density | g/cm3 | 1.68-1.73 |
| transverse strength | MPa | ≥11.0 |
| Young’ Modulus | GPa | ≤12.0 |
| Specific Resistance | µΩm | 5.2-6.5 |
| Maximum current density | KA/cm2 | 17-24 |
| Current Carrying Capacity | A | 17400-24000 |
| (C.T.E) | 10-6℃ | ≤2.0 |
| ash content | % | ≤0.2 |
| Typical Characteristics of Nipple (4TPI/3TPI) | ||
| Bulk Density | g/cm3 | 1.78-1.83 |
| transverse strength | MPa | ≥20.0 |
| Young’ Modulus | GPa | ≤15.0 |
| Specific Resistance | µΩm | 3.5-4.5 |
| (C.T.E) | 10-6℃ | ≤1.8 |
| ash content | % | ≤0.2 |
Product detail pictures:
Related Product Guide:
We're going to commit ourselves to giving our esteemed buyers using the most enthusiastically considerate solutions for Special Price for Graphite Electrode Plant - HP 350mm Graphite Electrode – Hexi, The product will supply to all over the world, such as: Durban, Iraq, French, Company name, is always regarding quality as company' s foundation, seeking for development via high degree of credibility , abiding by ISO quality management standard strictly, creating top-ranking company by spirit of progress-marking honesty and optimism.
By James Brown from Belgium - 2018.09.19 18:37
Superb technology, perfect after-sales service and efficient work efficiency, we think this is our best choice.
By Gabrielle from Azerbaijan - 2018.11.06 10:04